Page 830 - IGUS Bearing

iglidur iglidur
®
®
®
®
®
tribo iglidur tribo 3D printing | Tested iglidur tribofilament | Test results tribo
3D printing 3D printing
Printed as good as injection-moulded
®
iglidur 3D printing materials impress in Wear-resistant parts made of iglidur tribofilament with The following tests also show "printed as good as injection-
®
®
testing with injection-moulded quality the 3D printing method or parts made of iglidur i3 with the moulded": the 3D-printed iglidur plain bearings are
®
®
The igus test series prove that 3D-printed bearings made SLS method are much more wear-resistant than standard comparable to conventionally made plain bearings with
®
from iglidur tribo materials are just as wear-resistant as 3D printing materials. respect to wear resistance.
®
injection-moulded and machined parts. The tests have
also shown that iglidur 3D printing filaments, 3D printing
®
resins and SLS materials have significantly lower coefficient 20
of friction and up to 50 times higher abrasion resistance
than conventional 3D printing materials. This makes igus 15
®
3D printing materials the only ones that are convincing even
in moving applications. You can directly install printed parts 10
such as plain bearings, drive nuts or worm gears and use ABS printed
them as wear-resistant parts - from the prototype phase Wear rate [µm/km] 5
to series production. 0

ABS iglidur iglidur iglidur
®
®
®
printed i180 i3 J
printed printed moulded
Linear wear: p = 0.11MPa; v = 0.34m/s; l = 370mm iglidur i180 printed
®

50 1,000
45
40 800
35
30 600
Wear rate [µm/km] 20 3.0 3.0 2.0 2.0 0.7 2.0 10.0 15.0 279.0 269.0 66.0 49.0 20.0 14.0 24.0 26.0 Wear rate [µm/km] 400 ABS PA12
25
15
200
10
5
0
iglidur iglidur iglidur PA12 ABS PA66 POM PA66 0 ABS PA12 iglidur iglidur iglidur iglidur
®
®
®
®
®
®
®
i3 i150 i190 (SLS) (FDM) (moulded) (machined) (machined) (FDM) (SLS) i180 J260 i3 W300
(SLS) (FDM) (FDM) (FDM) (FDM) (SLS) moulded
®
®
Cf53 304 stainless steel Wear, rotating p =20MPa; v = 0.01m/s, 304 stainless iglidur i3 iglidur i180
Wear, 60° pivoting, p = 2MPa; v = 0.01m/s steel
50 300
45 250
40
35 200
30 150
Wear rate [µm/km] 20 2.0 4.0 1.2 0.4 2.0 2.0 10,000 8.0 95.0 163.0 104.0 47.0 4.0 1.2 57.0 9,999 Wear rate [µm/km] 100 iglidur i3 iglidur i180
25
15
®
®
10
50
5
0
®
®
®
®
®
®
iglidur iglidur iglidur PA12 ABS PA66 POM PA66 0 iglidur iglidur iglidur iglidur
®
i3 i150 i190 (SLS) (FDM) (moulded) (machined) (m) i3 i180 G W300
(SLS) (FDM) (FDM) printed printed moulded moulded
Cf53 304 stainless steel 10MPa 210MPa 45MPa
Wear, linear p = 1MPa; v = 0.01m/s ASEAN 09/2023 ASEAN 09/2023 Wear, pivoting shaft: 304 stainless steel, v = 0.01m/s; iglidur G iglidur W300
®
®
ß = 60°
828 Online tools and more information u www.igus-asean.com/idd Prices and delivery time online u www.igus-asean.com/tribofilament 829